Application:
Suitable for automotive ignition rings, motorbike ignition rings, sensors, and other electronic components package.
Characteristics:
Good insulation, high permeability, fluidity, heat resistance, surface gloss, and workmanship.
The property before curing:
| Appearance | Main agent A | Black viscous liquid (Color-Tunable) |
| Curing agent B | Brown liquid | |
| Density(25ºC) g/cm³ | Main agent A | 1.70-1.85 |
| Curing agent B | 1.10-1.20 | |
| Viscosity (40ºC, mPa.s) | Main agent A | 3000-5000 |
| Curing agent B | 15-35 |
The property after curing:
| Gel time (150ºC/s) | 170-210 |
| Glass Transition Temperature (ºC) | ≥130 |
| Linear Expansion Coefficient(ppm/k, lower than the average of Tg ) | ≤43 |
| Water Absorption(%, 100ºC/24h) | ≤0.7 |
| Thermal Conductivity (W/mK) | ≥0.60 |
| Insulation Strength (KV/mm) | ≥24 |
| Dielectric Constant (50Hz) | ≤3.8 |
| Volume Resistivity (Ω/cm) | ≥1.0×1016 |
Mixing Ratio
100:28
Packaging:
Component A: 30kg /barrel
Component B: 5kg /barrel
Storage Conditions:
The product should be sealed in its original packaging container and stored in a dry and ventilated place. In an environment of 18-40ºC, the shelf life is 6 months. If the shelf life is exceeded, analysis is required to determine whether it is still valid.
Due to the storage conditions, this product may experience a small amount of precipitation during storage, which is a normal phenomenon. After stirring evenly, it can be used normally.